以P25为原料,通过水解热解法制备得到二氧化钛纳米管(TN)。采用SEM和TEM分析了TN的形貌,TN的管径为6nm,长度为11.2μm。以氧化石墨、TN、硫酸亚铁为原料,通过一步水热合成法,制备得到石墨烯二氧化钛纳米管-铁水凝胶(GO-TN-H),将其冷冻干燥后得到石墨烯二氧化钛纳米管-铁气凝胶(GO-TN-G)。采用BET分析了TN和GO-TN-G的孔结构,结果表明,TN的平均孔径为14nm,孔的容积为0.6cm3/g,比表面积为160m2/g;GO-TN-G的比表面积为162m2/g。通过吸附等温线测定实验,研究了GO-TN-H对环丙沙星的吸附性能。GO-TN-H对环丙沙星的最大吸附容量可达750mg/g,Langmuir方程比Freundlich方程能更好拟合其吸附行为。结合SEM、TEM、BET等分析结果,推断认为水凝胶表面存在的官能团与环丙沙星表面基团之间的物理和化学吸附作用,使得GO-TN-H对环丙沙星有较强的吸附性能。该水凝胶吸附剂对环丙沙星的最大吸附容量是国内文献报道数值的33.5倍,是国外现有报道数值的11.5倍。该吸附剂具有制备过程简单,吸附量大,应用前景广阔等特点。
Abstract：Titanate nanotube(TN) was prepared by hydrolytic and pyrolytic method with P25 as raw material.SEM and TEM images showed that the diameter of TN was 6nm and the length was ranged from 1μm to 1.2μm.Graphenetitanate nanotube-Fe hydrogel(GO-TN-H) was prepared by hydrothermal synthesis method with graphite oxide(GO) TN and ferrous sulfate as raw materials,and then graphenetitanate nanotube-Fe aerogel(GO-TN-G) was obtained by freeze-drying.The pore characteristics of TN and GO-TN-G was obtained by BET method.The results showed that(1) the average pore diameter,pore volume and the specific surface area of TN was14 nm,0.6cm3/g and 160m2/g,respectively;(2) the specific surface area of GO-TN-G was 162m2/g.The adsorption isotherm of ciprofloxacin in aqueous solution onto GO-TN-H was investigated and the resultsindicated that the maximal adsorption capacity was 750mg/g,and the adsorption isotherm of GO-TN-H was better fitted with Langmuir model than with Freundlich model.The adsorption properties of GO-TN-H for ciprofloxacin were attributed to physical and chemical adsorption interaction between functional groups on the surface of hydrogels and groups of ciprofloxacin.The maximal adsorption capacity of ciprofloxacin onto GO-TN-H was 3 to 3.5 times of the recent data reported domestically,and 11.5 times of the latest results reported abroad.The adsorbent of GO-TN-H was a facile preparation technique with higher adsorption capacity and extensive application prospect.
[1]Kummerer K.Antibiotics in the aquatic environment-A review-Part I.Chemosphere[J].2009,75(4):417-434.
[2]Baquero F,Martinez J L,Canton R.Antibiotics and antibiotic resistance in water environments.Current Opinion in Biotechnology[J].2008,19(3):255-260.
[3]Wang Dan,Sui Qian,Zhao Wentao,et al.Pharmaceutical and personal care products in the surface water of China:A review.Chinese Science Bulletin[J].2014,59(5):743-751.
[4]Gu Cheng,Karthikeyan K G.Sorption of the antimicrobial ciprofloxacin to aluminum and iron hydrous oxides.Environmental Science&Technology[J].2005,39(23):9166-9173.
[5]Carabineiro S A C,Thavorn-Amornsri T,Pereira M F R,Figueiredo J L.Adsorption of ciprofloxacin on surface-modified carbon materials.Water Research[J].2011,45(15):4583-4591.
[6]Kumar K,Gupta S C,Chander Y,et al.Antibiotic use in agriculture and its impact on the terrestrial environment.Advances in Agronomy[J].2005,87(5):1-54.
[7]Liu Weifeng,Zhang Jian,Zhang Chenglu,et al.Sorption of norfloxacin by lotus stalk-based activated carbon and iron-doped activated alumina:Mechanisms,isotherms and kinetics.Chemical Engineering Journal[J].2011,171(2):431-438.
[8]Homem V,Santos L.Degradation and removal methods of antibiotics from aqueous matrices–Areview.Journal of Environmental Management[J].2011,92(10):2304-2347.
[9]Arslan-Alaton I,Dogruel S.Pre-treatment of penicillin formulation effluent by advanced oxidation processes.Journal of Hazardous Materials[J].2004,112(1/2):105-113.
[10]Yang Mingxuan,Ma Jie,Sun Yiran,et al.Synthesis of carbon nanotubes/Fe Sfenton-like catalyst and its catalytic properties.Chemical Journal of Chinese Universities-Chinese[J].2014,35(3):570-575.
[11]Chelliapan S,Wilby T,Sallis P J.Performance of an up-flow anaerobic stage reactor(UASR)in the treatment of pharmaceutical wastewater containing macrolide antibiotics.Water Research[J].2006,40(3):507-516.
[12]Chen W R,Huang C H.Adsorption and Transformation of Tetracycline Antibiotics with Aluminum Oxide.Chemosphere[J].2010,79(8):779-785.
[13]Wu Qingfeng,Li Zhaohui,Hong Hanlie.Influence of types and charges of exchangeable cations on ciprofloxacin sorption by montmorillonite.Journal of Wuhan University of Technology(Materials Science Edition)[J].2012,27(3):516-522.
[14]Koyuncu I,Arikan O A,Wiesner M R,et al.Removal of hormones and antibiotics by nanofiltration membranes.Journal of Membrane Science[J].2008,309(S1/2):94-101.
[15]Guo Changsheng,Ge Ming,Liu Lu,et al.Directed synthesis of mesoporous Ti O2microspheres:catalysts and their photocatalysis for bisphenol A degradation.Environmental Science&Technology[J].2010,44(1):419-425.
[16]Xiang Q,Yu J,Jaroniec M.Synergetic effect of Mo S2 and graphene as cocatalysts for enhanced photocatalytic H2production activity of Ti O2nanoparticles.Journal of the American Chemical Society[J].2012,134(15):6575-6578.
[17]彭小明,傅大放,秦庆东.竹炭表面改性对两种抗生素吸附性能的影响.东南大学学报(自然科学版)[J].2014,44(6):1271-1277.
[18]陆祎品,江淼,郑芳芳,等.多孔树脂及碳纳米管对环丙沙星的吸附行为与机理.化工学报[J].2012,63(11):3567-3573.
[19]高鹏,莫测辉,李彦文,等.高岭土对喹诺酮类抗生素吸附特性的初步研究.环境科学[J].2011,32(6):1740-1744.
[20]Zhuang Y,Yu F,Ma J,et al.Graphene as a template and structural scaffold for the synthesis of a 3D porous bio-adsorbent to remove antibiotics from water.RSC Advances[J].2015,5(35):27964-27969.
基本信息:
DOI：10.16026/j.cnki.iea.2016040368
中图分类号:TQ427.26;O647.3
引用信息:
[1]戴荣,郑兴业,曹力涛,等.石墨烯二氧化钛纳米管-铁水凝胶对环丙沙星吸附性能的研究[J].离子交换与吸附,2016,32(04):368-376.DOI:10.16026/j.cnki.iea.2016040368.
基金信息:
2015年度南京工程学院大学生科技创新项目基金(N20151201)